Study on Microstructure and Mechanical Properties of Low Cost Ti-Fe-B Alloy

Abstract

Microstructure evolution and mechanical properties of low cost Ti-2Fe-0.1B alloy under different heat treatment were studied. Results indicated that two kinds of equiaxed microstructures with different characteristics were obtained in conventional and double annealing, and typical lamellar microstructure was obtained in β annealing. Tensile test results shown that as-received rolled alloy possess highest strength and plasticity simultaneously due to fine and entangled microstructure. Uniform equiaxed dimples were observed in microstructure, which revealed ductile fracture morphology. Key words: titanium alloy; microstructure; heat treatment; mechanical properties