Effects of Filling Rate and Resin Concentration on Pore Characteristics and Properties of Carbon Based Wood Ceramics

Abstract

As a kind of novel porous ceramics, wood ceramics can be used for filtration, friction, energy storage and electrode materials, etc. In current work, the carbon based wood ceramics (C WCMs) was prepared using pine wood powder and phenolic resin as starting materials. The effects of filling rate of wood powder and resin concentration on pore characteristics and properties of C WCMs were characterized and analyzed with different techniques. Furthermore, the association among porosity of C WCMs, filling rate of wood powder and resin concentration was explored with multiple regression model. The results showed that: increasing the resin concentration and the filling rate of wood powder can improve the mechanical properties of C WCMs, but reduce the porosity and air permeability; when resin concentration is more than 50%, a large amount of caking will appear in the C WCMs, causing internal defects; changing the filling rate under a certain resin concentration can obtain the C WCMs with better pore structure; the porosity of C WCMs has a good linear relationship with resin concentration and filling rate, under the condition that sintering process and the size of wood powder are determined.

Keywords

• carbon based wood ceramics
• resin concentration
• filling rate
• pore characteristics
• properties
• multiple regression model