NiFe₂O₄/Ketjen Black Composites as Efficient Membrane Separators to Suppress the Shuttle Effect for Long-Life Lithium-Sulfur Batteries

Abstract

Lithium-sulfur batteries exhibit great potential as one of the most promising energy storage devices due to their high theoretical energy density and specific capacity. However, the shuttle effect of the soluble polysulfide intermediates could lead to a severe self-discharge effect that hinders the development of lithium-sulfur batteries. In this paper, a battery separator has been prepared based on NiFe2O4/Ketjen Black (KB) modification by a simple method to solve the shuttle effect and improve the battery performance. The as-modified separator with the combination of small-size KB and NiFe2O4 nanoparticles can effectively use the physical and chemical double-layer adsorption to prevent polysulfide from the shuttle. Moreover, it can give full play to its catalytic effect to improve the conversion efficiency of polysulfide and activate the dead sulfur. The results show that the NiFe2O4/KB-modified separator battery still maintains a discharge capacity of 406.27 mAh/g after 1000 stable cycles at a high current density of 1 C. Furthermore, the coulombic efficiency remains at 99%, and the average capacity attenuation per cycle is only 0.051%. This simple and effective method can significantly improve the application capacity of lithium-sulfur batteries.

Keywords

• lithium-sulfur battery
• nano NiFe₂O₄
• adsorption
• separator modification