Strength Properties and Damage Evolution Mechanism of Single-Flawed Brazilian Discs: An Experimental Study and Particle Flow Simulation

Abstract

Understanding the tensile strength properties and damage evolution mechanism in fissured rock is very important to fundamental research and engineering design. The effects of flaw dip angle on the tensile strength, macroscopic crack propagation and failure mode of symmetrical Brazilian discs of rock-like materials were investigated. A parallel bonding model was proposed to examine the damage of pre-flawed discs under splitting the load. The microscopic parameters of particles and bonds in the model that can characterize rock-like materials’ mechanical and deformation properties were obtained by calibrating against the laboratory test results. The crack development, energy evolution and damage characteristics of Brazil discs containing a single pre-existing flaw were studied at the microscopic scale. The results show that the flaw significantly weakens the strength of the Brazilian disc, and both the peak load and the initial cracking load decrease with increasing flaw angle. The failure modes of the rock-like specimens are mainly divided into three types: wing crack penetration damage mode, tensile-shear penetration damage mode and radial penetration failure mode. Except for the flaw dip angle 0°, the wing cracks generally sprouted at the tip of the pre-flaw, and the wing cracks at both tips of the pre-flaw are centrosymmetric. Crack coalescence was concentrated in the post-peak stage. Based on the particle flow code (PFC) energy partitions, the damage variables characterized by dissipation energy were proposed. The disc specimen’s pre-peak damage variables and peak damage variables decreased with increasing flaw angle, and the damage was concentrated in the post-peak phase.

Keywords

• rock-like materials
• Brazilian split test
• pre-flaw
• crack propagation
• particle flow code