Wettability of a Polymethylmethacrylate Surface by Fluorocarbon Surfactant Solutions

Abstract

To clarify the adsorption behavior of fluorocarbon surfactants on PMMA surfaces, the contact angles of two nonionic fluorocarbon surfactants (FNS-1 and FNS-2) and an anionic fluorocarbon surfactant (FAS) on polymethylmethacrylate (PMMA) surface were determined using the sessile drop method. Moreover, the effects of molecular structures on the surface tension, adhesion tension, solid–liquid interfacial tension, and adhesion work of the three fluorocarbon surfactants were investigated. The results demonstrate that the adsorption amounts for three fluorocarbon surfactants at the air–water interface are 4~5 times higher than those at the PMMA–solution interface. The three fluorocarbon surfactants adsorb on the PMMA surface by polar groups before CMC and by hydrophobic chains after CMC. Before CMC, FNS-2 with the smallest molecular size owns the highest adsorption amount, while FAS with large-branched chains and electrostatic repulsion has the smallest adsorption amount. After CMC, the three fluorocarbon surfactants form aggregates at the PMMA-liquid interface. FAS possesses the smallest adsorption amount after CMC. Besides, FNS-1 possesses a higher adsorption amount than FNS-2 due to the longer fluorocarbon chain and the lower CMC value of FNS-1. The adsorption behaviors of nonionic and anionic fluorocarbon surfactants on the PMMA surface are different. FAS forms interfacial aggregates before CMC, which may be attributed to the electrostatic interaction between the anionic head of FAS and the PMMA surface.

Keywords

• wettability
• polymethylmethacrylate
• contact angle
• fluorocarbon surfactant
• adsorption