Consequences of enamel preparation with sodium hypochlorite, polyacrylic and phosphoric acids for the bonding of brackets with resin-modified glass ionomer cements

Abstract

The aim of this study was to evaluate the effects of deproteinization with 5.25% sodium hypochlorite (NaOCl) prior to enamel conditioning with 10% polyacrylic acid (PAA) and 35% phosphoric acid (PA) on the bond strength (BS) of brackets bonded with resin-modified glass ionomer cement (RMGIC). One hundred human premolars extracted for orthodontic reasons were divided into 5 groups (n = 20 in each group): G1 (control), enamel conditioning with PA, application of adhesive and bonding of brackets with TransbondTM XT composite resin (3M/Unitek, Monrovia, CA, USA); G2, enamel conditioning with PAA and bonding with RMGIC (Fuji OrthoTM LC, GC America, Alsip, IL, USA); G3, NaOCl-treated enamel, conditioning with PAA and bonding with RMGIC; G4, enamel conditioning with PA and bonding with RMGIC; and G5, NaOCl-treated enamel, conditioning with PA and bonding with RMGIC. Once the brackets were bonded, the teeth were stored in distilled water for 24 hours at room temperature and pressure until being subjected to shear stress in a Universal Mechanical Testing Machine (EMIC® DL 500, São José dos Pinhais, PR, Brazil). The BS value was higher in G1 (17.08 ± 6.39) than in any of the experimental groups (p 0.05), except between G3 (9.86 ± 2.90) and G5 (5.00 ± 2.49). No statistically significant differences were noted between the mean Adhesive Remnant Index values among the evaluated groups (p > 0.05). Conclusion: The use of NaOCl combined with PAA increased the BS of brackets bonded with RMGIC. The deproteinization of the group treated with PA reduced the shear bond strength of the brackets.

Keywords

• bracket
• dental enamel
• glass ionomer cements