High-Efficiency Carbon Fiber Recovery Method and Characterization of Carbon FIBER-Reinforced Epoxy/4,4′-Diaminodiphenyl Sulfone Composites

Abstract

Globally, the demand for carbon fiber-reinforced thermosetting plastics for various applications is increasing. As a result, the amount of waste from CFRPs is increasing every year, and the EU Council recommends recycling and reuse of CFRPs. Epoxy resin (EP) is used as a matrix for CFRPs, and amine hardeners are mainly used. However, no research has been conducted on recycling EP/4,4’-diaminodiphenyl sulfone (DDS)-based CFRP. In this study, the effect of steam and air pyrolysis conditions on the mechanical properties of re-cycled carbon fiber (r-CF) recovered from carbon fiber-reinforced thermosetting (epoxy/4,4′-diaminodiphenyl sulfone) plastics (CFRPs) was investigated. Steam pyrolysis enhanced resin degradation relative to N2. The tensile strength of the recovered r-CF was reduced by up to 35.12% due to oxidation by steam or air. However, the interfacial shear strength (IFSS) tended to increase by 9.18%, which is considered to be due to the increase in functional groups containing oxygen atoms and the roughness of the surface due to oxidation. The recycling of CFRP in both a steam and an air atmosphere caused a decrease in the tensile strength of r-CF. However, they were effective methods to recover r-CF that had a clean surface and increased IFSS.

Keywords

• carbon fiber-reinforced plastic (CFRP)
• recycling
• epoxy
• DDS
• mechanical properties