Ultrasonic Welding of Additively Manufactured PEEK and Carbon-Fiber-Reinforced PEEK with Integrated Energy Directors

Abstract

The thermoplastic polymer polyether ether ketone (PEEK) offers thermal and mechanical properties comparable to thermosetting polymers, while also being thermally re-processable and recyclable as well as compatible with fused filament fabrication (FFF). In this study, the feasibility of joining additively manufactured PEEK in pure and short carbon-fiber-reinforced form (CF-PEEK) is investigated. Coupon-level samples for both materials were fabricated using FFF with tailored integrated welding surfaces in the form of two different energy director (ED) shapes and joined through ultrasonic polymer welding. Using an energy-driven joining process, the two materials were systematically investigated with different welding parameters, such as welding force, oscillation amplitude and welding power, against the resulting weld quality. The strengths of the welded bonds were characterized using lap-shear tests and benchmarked against the monotonic properties of single 3D-printed samples, yielding ultimate lap-shear forces of 2.17kN and 1.97kN and tensile strengths of 3.24MPa and 3.79MPa for PEEK and CF-PEEK, respectively. The weld surfaces were microscopically imaged to characterize the failure behaviors of joints welded using different welding parameters. Samples welded with optimized welding parameters exhibited failures outside the welded region, indicating a higher weld-strength compared to that of the bulk. This study lays the foundation for using ultrasonic welding as a glue-free method to join 3D-printed high-performance thermoplastics to manufacture large load-bearing, as well as non-load-bearing, structures, while minimizing the time and cost limitations of FFF as a fabrication process.

Keywords

• fused filament fabrication
• ultrasonic welding
• PEEK
• carbon-fiber-reinforced PEEK
• lap-shear strength
• glue-free joining