Intense Red Catho- and Photoluminescence from 200 nm Thick Samarium Doped Amorphous AlN Thin Films

Abstract

Abstract Samarium (Sm) doped aluminum nitride (AlN) thin films are deposited on silicon (100) substrates at 77 K by rf magnetron sputtering method. Thick films of 200 nm are grown at 100–200 watts RF power and 5–8 m Torr nitrogen, using a metal target of Al with Sm. X-ray diffraction results show that films are amorphous. Cathodoluminescence (CL) studies are performed and four peaks are observed in Sm at 564, 600, 648, and 707 nm as a result of4G5/2 → 6H5/2,4G5/2 → 6H7/2,4G5/2 → 6H9/2, and4G5/2 → 6H11/2transitions. Photoluminescence (PL) provides dominant peaks at 600 and 707 nm while CL gives the intense peaks at 600 nm and 648 nm, respectively. Films are thermally activated at 1,200 K for half an hour in a nitrogen atmosphere. Thermal activation enhances the intensity of luminescence.

Keywords

• Cathodoluminescence
• Photoluminescence
• Thermal activation
• XRD
• Samarium
• AlN