Trimming flow, plasticity, and mechanical properties by cubic silsesquioxane chemistry

Abstract

Abstract In this work, the possibility of managing the rheological and mechanical parameters of composites based on PLA with the use of cubic structures of organofunctional spherosilicates was verified. To accurately observe the effect of various organosilicon modifier substitutions on changes in composites’ properties, we synthesized and used monofunctional octasubstituted derivatives as reference systems. The OSS/PLA systems were tested with concentrations of 0.1–2.5% (w/w) using extrusion to obtain a filament with a diameter of 1.75 mm. The printed samples underwent comprehensive tests including microscopic (SEM–EDS, optical microscope), rheological, thermal (TG, DSC, HDT), mechanical (impact and strength) as well as water contact angle tests. The work is interdisciplinary in nature and combines elements of organosilicon synthesis, materials engineering, and materials processing and characterization technology.