Electrode performance of amorphous MoS3 in all-solid-state sodium secondary batteries

Abstract

All-solid-state Na–S secondary batteries that use sodium and sulfur, both available in abundance, are the most attractive next-generation batteries. In this study, two types of amorphous MoS3 (a-MoS3) were prepared as electrode active materials for use in all-solid-state sodium secondary batteries using the thermal decomposition (TD) of (NH4)2MoS4 and mechanochemical (MC) processes, denoted a-MoS3 (TD) and a-MoS3 (MC), respectively. X-ray diffraction, thermogravimetric-differential thermal analysis, and X-ray photoelectron spectroscopy (XPS) analyses revealed that a-MoS3 (TD) and a-MoS3 (MC) had different local structures. The a-MoS3 (TD) and a-MoS3 (MC) electrodes showed high reversible capacities of 310 mAh g−1 and 260 mAh g−1, respectively, for five cycles in all-solid-state sodium secondary batteries. XPS analysis of the discharge–charge products suggested that the dissociation and formation of disulfide bonds occurred during the discharge–charge reaction. The results show that a-MoS3 is a promising active electrode material for all-solid-state sodium batteries.

Keywords

• Molybdenum sulfides
• Amorphous
• Solid electrolytes
• Sodium batteries
• All-solidstate batteries