Effect of Nitrate/Bromide on the Hydration Process of Cement Paste Mixed with Alkali Free Liquid Accelerator at Low Temperature

Abstract

The effects of different inorganic salt accelerators (CaBr2, NaBr, Ca(NO3)2, NaNO3) and an alkali-free liquid accelerator were researched at a low temperature of 10 °C. The results showed the effects of 1.5% NaBr and 1.5% NaNO3 inorganic accelerator were pronounced. The 1-d compressive strengths of the mortar with these two inorganic salts were increased by 185.8% and 184.2%, respectively, and the final setting times were shortened from 7.74 to 6.08 min and 6.12 min, respectively. The hydration temperatures at 10 °C were measured, and the promotion effects of the inorganic accelerators were calculated: the relationship between the hydration degree was αAS + NN > αAS + NB > αAS + CB > αAS + CN > αAS. In addition, the reaction of C3A with NaBr and NaNO3 was used to analyze the products in an ettringite phase, i.e., Ca4Al2O6Br210·H2O, 3CaOAl2O3Ca(NO3)2X·H2O. The formation of these phases was detected in the hydration products of the cement paste hydration for 12 h, 24 h, and 28 d. Combined with the mass loss of the ettringite phase at 90–120 °C, determined using TG/DTG, the synergetic acceleration mechanism of the inorganic accelerators was comprehensively inferred.

Keywords

• acceleration
• ettringite phase
• low temperature
• mechanism