Property Evaluation of AA2014 Reinforced with Synthesized Novel Mixture Processed through Squeeze Casting Technique

Abstract

Aluminum alloy–graphene metal matrix composite is largely used for structural applications in the aerospace and space exploration sector. In this work, the preprocessed powder particles (AA 2014 and graphene) were used as a reinforcement material in a squeeze casting process. The powder mixture contained aluminum alloy powder 2014 with an average particle size of 25 μm and 0.5 wt% graphene nano powder (Grnp) with 10 nm (average) particle size. The powder mixture was mixed using the high-energy planetary ball milling (HEPBM) technique. The experimental results indicated that the novel mixture (AA 2014 and graphene powder) acted as a transporting agent of graphene particles, allowing them to disperse homogeneously in the stir pool in the final cast, resulting in the production of an isotropic composite material that could be considered for launch vehicle structural applications. Homogeneous dispersion of the graphene nanoparticles enhanced the interfacial bonding of 2014 matrix material, which resulted in particulate strengthening and the formation of a fine-grained microstructure in the casted composite plate. The mechanical properties of 0.5 wt% graphene-reinforced, hot-rolled composite plate was strengthened by the T6 condition. When compared to the values of unreinforced parent alloy, the ultimate tensile strength and the hardness value of the composite plate were found to be 420 MPa and 123 HRB, respectively.

Keywords

• aluminum alloy 2014
• graphene
• squeeze casting
• hot rolling