Unveiling the Magnetic and Structural Properties of (X₂YZ; X = Co and Ni, Y = Fe and Mn, and Z = Si) Full-Heusler Alloy Microwires with Fixed Geometrical Parameters

Abstract

We studied Ni2FeSi-, Co2FeSi-, and Co2MnSi-based full-Heusler alloy glass-coated microwires with the same geometric parameters, i.e., fixed nucleus and total diameters, prepared using the Taylor–Ulitovsky method. The fabrication of X2YZ (X = Co and Ni, Y = Fe and Mn, and Z = Si)-based glass-coated microwires with fixed geometric parameters is quite challenging due to the different sample preparation conditions. The XRD analysis showed a nanocrystalline microstructure for all the samples. The space groups Fm3¯m (FCC) and Im3¯m (BCC) with disordered B2 and A2 types are observed for Ni2FeSi and Co2FeSi, respectively. Meanwhile, a well-defined, ordered L21 type was observed for Co2MnSi GCMWs. The change in the positions of Ni, Co and Mn, Fe in X2YSi resulted in a variation in the lattice cell parameters and average grain size of the sample. The room-temperature magnetic behavior showed a dramatic change depending on the chemical composition, where Ni2FeSi MWs showed the highest coercivity (Hc) compared to Co2FeSi and Co2MnSi MWs. The Hc value of Ni2FeSi MWs was 16 times higher than that of Co2MnSi MWs and 3 times higher than that of Co2FeSi MWs. Meanwhile, the highest reduced remanence was reported for Co2FeSi MWs (Mr = 0.92), being about 0.82 and 0.22 for Ni2FeSi and Co2MnSi MWs, respectively. From the analysis of the temperature dependence of the magnetic properties (Hc and Mr) of X2YZ MWs, we deduced that the Hc showed a stable tendency for Co2MnSi and Co2FeSi MWs. Meanwhile, two flipped points were observed for Ni2FeSi MWs, where the behavior of Hc changed with temperature. For Mr, a monotonic increase on decreasing the temperature was observed for Co2FeSi and Ni2FeSi MWs, and it remained roughly stable for Co2MnSi MWs. The thermomagnetic curves at low magnetic field showed irreversible magnetic behavior for Co2MnSi and Co2FeSi MWs and regular ferromagnetic behavior for Ni2FeSi MWs. The current result illustrates the ability to tailor the structure and magnetic behavior of X2YZ MWs at fixed geometric parameters. Additionally, a different behavior was revealed in X2YZ MWs depending on the degree of ordering and element distribution. The tunability of the magnetic properties of X2YZ MWs makes them suitable for sensing applications.

Keywords

• full-Heusler alloys
• glass-coated microwires
• magnetic behavior
• sensing applications