Effect of Milling Time and Reinforcement Volume Fraction on Microstructure and Mechanical Properties of SiC_p-Reinforced AA2017 Composite Powder Produced by High-Energy Ball Milling

Abstract

The influence of milling time and volume fraction of reinforcement on the morphology, microstructure, and mechanical behaviors of SiCp-reinforced AA2017 composite powder produced by high-energy ball milling (HEBM) was investigated. AA2017 + SiCp composite powder with different amounts of SiC particles (5, 10, and 15 vol%) was successfully prepared from gas-atomized AA2017 aluminum alloy powder with a particle size of 300 nm to 68 nm, 64 nm, and 64 nm after 5 h of milling, corresponding to SiC contents of 5, 10, and 15 vol%, respectively. As a result, the lattice strain increased from 0.15% to 0.5%, which is due to significant plastic deformation during the ball milling process. XRD results showed a rapid decrease in crystallite size during the early milling phase, and the minimum grain size was achieved at a higher volume fraction of SiC particles. Microhardness tests revealed that the milling time has a greater influence on the hardness than the amount of SiC reinforcements. Therefore, the composite powder milled for 5 h showed an average microhardness three times higher than that of the unmilled powder particles.

Keywords

• composite powder
• high-energy ball milling
• crystallite size
• lattice strain
• microhardness