Preparation and Electrothermal Properties of Graphene Electrothermal Composite Floor

Abstract

Conventional electrothermal floors suffer from low heating efficiency, uneven temperature distribution across the floor surface, local overheating, and severe heat accumulation. In order to improve the heating performance, an electrothermal composite floor with graphene as the heating layer was fabricated. The relationship between time and temperature rise, the relationship between power density and temperature rise, running stability, and surface temperature distribution were investigated and analyzed after heating, and the surface temperature profiles were simulated in two and three dimensions. The results were compared with the carbon fiber electrothermal composite floor and the resistance wire electrothermal composite floor. The results indicated that the temperature of the graphene electrothermal composite floor rose to 27.1 °C, the electrothermal conversion efficiency reached 90.1% after 40 min of electrification, and the temperature distribution unevenness was 4.4 °C, which were better than the carbon fiber electrothermal composite floor and the resistance wire electrothermal composite floor. The graphene electrothermal composite floor exhibited high heating performance, thus aiding the development and manufacture of such composite flooring.

Keywords

• graphene
• electrothermal composite floor
• electrothermal performance
• surface temperature