Enhanced Photocatalytic Degradation of Rhodamine-B under Led Light Using CuZnAl Hydrotalcite Synthesized by Co-Precipitation Technique

Abstract

The co-precipitation method was employed to synthesize a set of ZnAl hydrotalcite materials modified by Cu2+. The synthesized materials have a similar lamellar structure to that of hydrotalcite. The distance between layers is in the range of 7.73–8.56 Å. The network parameters a and c ranged from 3.058 to 3.074 Å and from 23.01 to 24.44, respectively. According to the IUPAC classification, the composites possess a mesoporous structure which belongs to class IV, type H 3. Particularly, the absorption edge shifts strongly to the visible light region when increasing the molar ratio of Cu2+ in the samples from 0 to 3.5. The photocatalytic activity of the synthetic materials was evaluated through the degradation efficiency of rhodamine-B (Rh-B) in the water and colorants in textile wastewater. The present study was the first to synthesize a material sample that contains a molar ratio of Cu2+ in the range of 2.5–3.5 and has high catalytic activities. They were able to degrade Rh-B at a high concentration (100 ppm) with a conversion rate of approximately 90% after 240 min of irradiation using a 30 W LED light. The catalytic activity of the composites depends on the molar ratio of modified Cu2+, the value of environmental pH, the H2O2 concentration and the irradiation time.

Keywords

• photocatalyst
• degradation
• rhodamine-B
• co-precipitation
• characterization