Mechanical and Tribological Behavior of Nitrided AISI/SAE 4340 Steel Coated with NiP and AlCrN

Abstract

In this study, novel surface engineering strategies to improve the wear performance of AISI 4340 were investigated. The strategies were as follows: (i) NiP deposition on a previously nitrided steel substrate, followed by NiP interdiffusion heat treatment at either 400 °C or 610 °C (referred to as duplex treatment); (ii) the deposition of AlCrN PVD coating on NiP layers on a previously nitrided steel substrate (referred to as triplex treatment). Prior to the deposition of AlCrN, the NiP was subjected to the interdiffusion heat treatment at either 400 °C or 610 °C. These strategies were compared with the performance of the AlCrN coating directly applied on nitrided steel. To characterize the microstructural features of each layer, X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy-dispersive X-ray spectroscopy (EDS) analysis were conducted. We also carried out mechanical and tribological behavior assessments. The tribological tests were carried out using a ball-on-disc tribometer under a constant load of 20 N and a tangential speed of 25 cm/s; cemented carbide spheres with a diameter of 6 mm were the counterpart body. The friction coefficient was continuously monitored throughout the tests. The results reveal that the wear mechanism for the AlCrN coating is predominantly oxidative. The most wear-resistant surface architecture was the one comprising AlCrN over the NiP layer subjected to interdiffusion heat treatment at either 400 °C or 610 °C.

Keywords

• AlCrN/NiP tribological behavior
• AlCrN/NiP mechanical properties
• duplex treatment
• triplex treatment
• electroless nickel