Ruthenium Catalysts Templated on Mesoporous MCM-41 Type Silica and Natural Clay Nanotubes for Hydrogenation of Benzene to Cyclohexane

Abstract

Mesoporous ruthenium catalysts (0.74–3.06 wt%) based on ordered Mobil Composition of Matter No. 41 (MCM-41) silica arrays on aluminosilicate halloysite nanotubes (HNTs), as well as HNT-based counterparts, were synthesized and tested in benzene hydrogenation. The structure of HNT core-shell silica composite-supported Ru catalysts were investigated by transmission electron microscopy (TEM), X-ray fluorescence (XRF) and temperature-programmed reduction (TPR-H2). The textural characteristics were specified by low-temperature nitrogen adsorption/desorption. The catalytic evaluation of Ru nanoparticles supported on both the pristine HNTs and MCM-41/HNT composite in benzene hydrogenation was carried out in a Parr multiple reactor system with batch stirred reactors (autoclaves) at 80 °C, a hydrogen pressure of 3.0 MPa and a hydrogen/benzene molar ratio of 3.3. Due to its hierarchical structure and high specific surface area, the MCM-41/HNT composite provided the uniform distribution and stabilization of Ru nanoparticles (NPs) resulted in the higher specific activity and stability as compared with the HNT-based counterpart. The highest specific activity (5594 h−1) along with deep benzene hydrogenation to cyclohexane was achieved for the Ru/MCM-41/HNT catalyst with a low metal content.

Keywords

• ruthenium catalysts
• benzene hydrogenation
• MCM-41
• halloysite nanotubes
• mesoporous aluminosilicates
• MCM-41/HNT composite