Investigating the microstructure and mechanical properties of deposited metal with ENiCrFe-7 covered electrode

Abstract

The effect of post weld heat treatment (PWHT) on microstructure and mechanical properties of deposited metal using ENiCrFe-7 covered electrode was investigated. The PWHT was conducted at 615 °C for 24 h. The results showed that three types of precipitates existed in both as-welded and PWHT deposited metals, i.e., NbC carbides, Al-Ti oxides in grains, and M _23 C _6 carbides on grain boundaries. The M _23 C _6 carbides coarsened after PWHT. The room temperature and elevated temperature (350 °C) tensile strength decreased by about 30 MPa, and elongation increased by about 3%–4% after PWHT. The tensile specimens presented ductile fracture feature and the dimples in PWHT condition were larger than that in as-welded condition. The hardness of deposited metal in as-welded condition was higher than that of PWHT condition. The impact toughness showed no significant change after PWHT. Both as-welded and PWHT impact specimens showed a mixed fracture mode with dominant ductile fracture and cleavage fracture.

Keywords

• ENiCrFe-7
• deposited metal
• microstructure
• mechanical properties
• PWHT