A New Systematic Approach Based on Dilatometric Analysis to Track Bainite Transformation Kinetics and the Influence of the Prior Austenite Grain Size

Abstract

This investigation explores the influence of the austenitisation heat treatment and thus, of the prior austenite grain size (PAGS), on the kinetics of the bainitic transformation, using as A case study two high-carbon, high-silicon, bainitic steels isothermally transformed (TIso = 250, 300, 350 °C), after being austenised at different temperatures (γTγ = 925–1125 °C). A methodology, based on the three defining dilatometric parameters extracted from the derivative of the relative change in length, was proposed to analyse the transformation kinetics. These parameters are related to the time to start bainitic transformation, the time lapse for most of the transformation to take place and the transformation rate at the end of the transformation. The results show that increasing the PAGS up to 70 µm leads to an increase in the bainite nucleation rate, this effect being more pronounced for the lowest TIso. However, the overall transformation kinetics seems to be weakly affected by the applied heat treatment (γTγ and TIso). In one of the steels, PAGS > 70 µm (γTγ > 1050 °C), which weakly affects the progress of the transformation, except for TIso = 250 °C, for which the enhancement of the autocatalytic effect could be the reason behind an acceleration of the overall transformation.

Keywords

• bainite
• transformation kinetics
• austenitisation temperature
• austenite grain size
• full width at half maximum