With PBDB-T as the Donor, the PCE of Non-Fullerene Organic Solar Cells Based on Small Molecule INTIC Increased by 52.4%

Abstract

At present, most high-performance non-fullerene materials are centered on fused rings. With the increase in the number of fused rings, production costs and production difficulties increase. Compared with other non-fullerenes, small molecule INTIC has the advantages of easy synthesis and strong and wide infrared absorption. According to our previous report, the maximum power conversion efficiency (PCE) of an organic solar cell using PTB7-Th:INTIC as the active layer was 7.27%. In this work, other polymers, PTB7, PBDB-T and PBDB-T-2F, as the donor materials, with INTIC as the acceptor, are selected to fabricate cells with the same structure to optimize their photovoltaic performance. The experimental results show that the optimal PCE of PBDB-T:INTIC based organic solar cells is 11.08%, which, thanks to the open voltage (VOC) increases from 0.80 V to 0.84 V, the short circuit current (JSC) increases from 15.32 mA/cm2 to 19.42 mA/cm2 and the fill factor (FF) increases from 60.08% to 67.89%, then a 52.4% improvement in PCE is the result, compared with the devices based on PTB7-Th:INTIC. This is because the PBDB-T:INTIC system has better carrier dissociation and extraction, carrier transportation and higher carrier mobility.

Keywords

• polymer solar cells (pscs)
• non-fullerene small molecule acceptor
• synthesize easily
• strong and wide infrared absorption
• carrier mobility
• carrier transportation and extraction