Precipitation Processes during Non-Isothermal Ageing of Fine-Grained 2024 Alloy

Abstract

Mechanical alloying and powder metallurgy procedures were used to manufacture very fine-grained bulk material made from chips of the 2024 aluminum alloy. Studies of solution treatment and precipitation hardening of as-received material were based on differential scanning calorimetry (DSC) tests and TEM/STEM/EDX structural observations. Structural observations complemented by literature data lead to the conclusion that in the case of highly refined structure of commercial 2024 alloys prepared by severe plastic deformation, typical multi-step G-P-B →θ” →θ’ →θ precipitation mechanism accompanied with G-P-B →S” →S’ →S precipitation sequences result in skipping the formation of metastable phases and direct growth of the stable phases. Exothermic effects on DSC characteristics, which are reported for precipitation sequences in commercial materials, were found to be reduced with increased milling time. Moreover, prolonged milling of 2024 chips was found to shift the exothermic peak to lower temperature with respect to the material produced by means of common metallurgy methods. This effect was concluded to result from preferred heterogeneous nucleation of particles at subboundaries and grain boundaries, enhanced by the boundary diffusion in highly refined structures.

Keywords

• AA2024 alloy
• scrap metal milling
• structure refining
• powder metallurgy
• precipitation hardening