Research on deformation behaviors at different temperatures of lean duplex stainless steel S32101 produced by direct cold rolling process

Abstract

In this paper, the mechanical properties, work hardening characteristics and deformation mechanism of lean duplex stainless steel (LDSS) S32101 produced by direct cold rolling were studied under different temperature conditions. The yield strength (YS) and tensile strength (TS) of S32101 decreased with the increase of deformation temperature, while the elongation increased first and then decreased. The TS of S32101 at −70 °C was 1052.6 MPa, the elongation remained 57.2%, and the product of strength and elongation (PSE) was as high as 60.2 GPa·%, which was mainly due to the synergistic strengthening of transformation induced plasticity (TRIP) and twinning-induced plasticity (TWIP) effects in austenite at cryogenic temperatures. The efficiency of grain refinement at cryogenic temperature was improved by TRIP effect and deformation twins (DTs), indicating that it had the potential to be applied at low temperature (−70 ∼ −30°C). Moreover, the high density nanotwins and the strong interaction between the dislocation and nanotwin bundles also contributed to strain hardening at low temperatures and thus better comprehensive mechanical properties could be achieved.

Keywords

• Lean duplex stainless steel
• Cryogenic mechanical properties
• Deformation behavior
• TRIP effect