Properties of Pb1–xBax(Zr1–yTiy)1–zSnzO3 (x = 0.03, y = 0.02, z = 0÷0.08) Ceramics

Abstract

This paper presents the results of obtaining and investigations of Pb1–xBax(Zr1–yTiy)1–zSnzO3 (PBZTS) ceramics with constant x = 0.03 and y = 0.02, and variable z = 0, 0.04, 0.06 and 0.08 (abbreviations of the samples were following PBZTS0, PBZTS4, PBZTS6, PBZTS8, respectively). The investigated compositions are close to rhombohedral-orthorhombic morphotropic phase boundary. The ceramic samples have been obtained by conventional ceramic technology from simple oxides PbO, ZrO2, TiO2, SnO2 and barium carbonate BaCO3. The ceramic powders, after calcination, have been pressed into discs and sintered using free sintering (FS) method. For samples obtained in such a way, the dielectric properties at various frequencies and electrical conductivity have been investigated. The increase of Sn content orders the microstructure of ceramics, and as a result the improvement of the dielectric properties of ceramic samples can be obtained.

Keywords

• pbzt and pbzts ceramics
• phase transitions
• dielectric properties
• electrical conductivity