Electrical Monitoring as a Novel Route to Understanding the Aging Mechanisms of Carbon Nanotube-Doped Adhesive Film Joints

Abstract

Carbon fiber-reinforced plastic bonded joints with novel carbon nanotube (CNT) adhesive films were manufactured and tested under different aging conditions by varying the surfactant content added to enhance CNT dispersion. Single lap shear (SLS) tests were conducted in their initial state and after 1 and 2 months immersed in distilled water at 60 °C. In addition, their electrical response was measured in terms of the electrical resistance change through thickness. The lap shear strength showed an initial decrease due to plasticization of weak hydrogen bonds, and then a partial recovery due to secondary crosslinking. This plasticization effect was confirmed by differential scanning calorimetry analysis with a decrease in the glass transition temperature. The electrical response varied with aging conditions, showing a higher plasticity region in the 1-month SLS joints, and a sharper increase in the case of the non-aged and 2-month-aged samples; these changes were more prevalent with increasing surfactant content. By adjusting the measured electrical data to simple theoretical calculations, it was possible to establish the first estimation of damage accumulation, which was higher in the case of non-aged and 2-month-aged samples, due to the presence of more prevalent brittle mechanisms for the CNT-doped joints.

Keywords

• carbon nanotubes
• aging
• structural health monitoring
• water uptake
• adhesive film
• surfactant