Aberration corrected scanning transmission electron microscopy is used to directly observe atom columns in an epitaxial BaTiO3 thin film deposited on a 3.6 nm-thick SrRuO3 electrode layer above an SrTiO3 (001) substrate. Compositional gradients across the heterointerfaces were examined using electron energy-loss spectroscopy techniques. It was found that a small amount of Ba and Ti had diffused into the SrRuO3 layer, and that this layer contained a non-negligible concentration of oxygen vacancies. Such point defects are expected to degrade the electrode’s electronic conductivity drastically, resulting in a much longer screening length. This may explain the discrepancy between experimental measurements and theoretical estimates of the ferroelectric critical thickness of a BaTiO3 ferroelectric barrier sandwiched between metallic SrRuO3 electrodes, since theoretical calculations generally assume ideal (stoichiometric) perovskite SrRuO3.