The Effect of Electropulsing Treatment on Properties of Pre-compressed AZ31 Magnesium Alloy

Abstract

The effect of electropulsing treatment (EPT) on quasi-static compression behavior and anisotropy of AZ31 Mg alloy were investigated based on quasi-static compression test. The results show that the orientation of the sample has a significant effect on the deformation mechanism of metal and this mechanism can be changed by pre-deformation and EPT. However, the strain rate sensitivity of the material is not affected by pre-deformation. Compared with the as-received plates, the anisotropy of AZ31 Mg alloy increased in ND-RD plane after pre-compression along the transverse direction, the ∆YS of specimens increased from 87 MPa to 98 MPa. After EPT, the anisotropy of AZ31 Mg alloy gradually decreased with the change of EPT temperature and EPT time, the ∆YS of the sample reached 14.2 MPa when EPT conducted at 200 ℃ for 15 min, which decreased 72.8 MPa compared with the as-received plates.

Keywords

• AZ31 Mg alloy
• Mechanical properties
• Pre-compression
• Anisotropy
• Deformation mechanism