Enhancing Flame Retardancy in Epoxy Resin with Clever Self-Assembly Method for Optimizing Interface Interaction via Well-Dispersed Cerium Oxide on Piperazine Pyrophosphate

Abstract

Developing flame-retardant epoxy resins (EPs) is essential to broaden their industrial applications, as their inherent flammability restricts their widespread use. In this study, commercial cerium oxide (CeO2) nanoparticles were modified with oleic acid and successfully assembled onto the surface of pyrophosphate piperazine (PAPP) through a simple solvophobic effect, constructing an integrated superstructure flame retardant, CeO2@PAPP, with enhanced performance integration. Compared to traditional simple blends, the EP composite with 10 wt% CeO2@PAPP displayed superior flame retardancy, thanks to the more subtle synergistic effects between flame retardant components and their favorable interface interactions. The EP composite achieved a UL-94 V-0 rating and increased the limiting oxygen index (LOI) to 34.2%. Significant reductions of 56.3% in peak heat release rate (PHRR) and 38.2% in total heat release (THR) were observed. Furthermore, total smoke release (TSR), carbon monoxide yield (COPR), and carbon dioxide yield (CO2PR) decreased by 52.2%, 50.2%, and 67.3%, respectively. Through comprehensive and detailed characterization, it was discovered that the assembled integrated CeO2@PAPP flame retardant can perform better in both the gas phase and condensed phase, resulting in superior flame-retardant properties. This study offers an effective strategy for developing highly flame-retardant EPs, thereby expanding their potential applications across various industries.

Keywords

• self-assembly
• flame retardancy
• rare earth
• synergistic effect
• epoxy resin