Performance comparison of flip-chip blue-light microLEDs with various passivation

Abstract

Abstract In this study, arrays of μLEDs in four different sizes (5 × 5 μm2, 10 × 10 μm2, 25 × 25 μm2, 50 × 50 μm2) were fabricated using a flip-chip bonding process. Two passivation processes were investigated with one involving a single layer of SiO2 deposited using plasma-enhanced chemical vapor deposition (PECVD) and the other incorporating Al2O3 deposited by atomic layer deposition (ALD) beneath the SiO2 layer. Owing to superior coverage and protection, the double-layers passivation process resulted in a three-order lower leakage current of μLEDs in the 5 μm chip-sized μLED arrays. Furthermore, higher light output power of μLEDs was observed in each chip-sized μLED array with double layers passivation. Particularly, the highest EQE value 21.9% of μLEDs array with 5 μm × 5 μm chip size was achieved with the double-layers passivation. The EQE value of μLEDs array was improved by 4.4 times by introducing the double-layers passivation as compared with that of μLEDs array with single layer passivation. Finally, more uniform light emission patterns were observed in the μLEDs with 5 μm × 5 μm chip size fabricated by double-layer passivation process using ImageJ software.

Keywords

• Blue light
• Micro-LED
• Double layers passivation
• Atomic layer deposition
• Flip-chip bonding