Scaffolds of PDLLA/bioglass 58S produced via selective laser sintering

Abstract

Scaffolds of PDLLA were produced to be implemented in maxilofacial surgeries inducing bone repair and regeneration. To prepare these scaffolds, bioglass (BG58S) was synthesized by sol-gel method, in order to be applied as osteoconductive dispersed particles in PDLLA matrix. Once presenting greater facility on parts fabrication, this polymeric matrix enables complex geometries production besides presenting compatible degradation rate for scaffold absorption and bone regeneration. Scaffolds production was performed by selective laser sintering in order to obtain tailored-made parts. FTIR and XRD analyses were carried out to observe the composition and evaluate the presence of crystalized phases in bioglass, obtaining Wollastonite. SEM was used to observe the BG particle distribution in PDLLA matrix and flexural test was performed to evaluate the composite mechanical properties. Results showed that was possible to obtain pieces using SLS method and with addition of 10%wt BG to polymeric matrix, flexural modulus and strength increased regarding to pure polymer.

Keywords

• scaffold
• bioglass
• PDLLA
• selective laser sintering (SLS)