Polyamide 12/E-glass Fabric Composite Production with Dip-coating

Abstract

In this study PA12 was reinforced with E-glass woven fabric by dip-coating. PA12 powder and ethanol suspensions were prepared with ratios at 30, 40 and 50% of powder to obtain different fibre contents. Coated fabrics were laid-up and kept in oven at 60°C to evaporate ethanol. Then it was placed in a compression mould and pressed. Obtained laminates were subjected to tensile, bending and impact tests. Fractured surfaces were observed. It was found that mechanical properties were highest when 40% PA powder used in suspension with dip-coating with additional lamination. Fibre failure and fibre pull-out were observed on fractured surfaces.