Grain Refinement by Extension Twin in Mg Alloy during Asymmetrical Rolling

Abstract

The work looked into the grain refinement process of Mg alloy during asymmetrical rolling with a focus on the role of twin. The present sample was deformed at ambient temperature by single operation with the height reduction of 50% at the roll speed ratio of 1:4 for the upper and lower rolls having the same dimension. From the electron backscatter diffraction analysis in the surface region where intense shear strain was imparted, a number of { 10 1 ¯ 2 } extension twins with a width of ~1 µm were detected clearly in most of the deformed grains. Moreover, the average misorientation angle of the deformed grains in the top region was found to be ~32°, which was two times higher than that in the center area where the extension twin was detected rarely. As a result, the microstructure in the top region was refined significantly down to be ~1.1 µm with an aid of twin activities that would be discussed in this study.

Keywords

• Mg alloy
• grain refinement
• asymmetrical rolling
• twin
• misorientation