Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 1999)
Engrosamiento anormal de partículas submicronicas de BaTiO<sub>3</sub> durante la primera etapa de sinterización
Abstract
The aim of the present paper is to describe the phenomena observed during sintering of submicronic BaTiO3 particles. For this purpose, constant heating rate experiments have been done at 10ºC/min up to 1400ºC. According to the behaviour observed on the shrinkage curves, several samples were quenched at different temperatures and their microstructures on fracture surfaces were studied by SEM. During the initial sintering of submicronic BaTiO3 particles, abnormal coarsening up to twice their initial size was observed. Such a coarsening could improve material densification by a coarsening-re-packing mechanism.En el presente trabajo se aborda la descripción de los fenómenos observados durante la sinterización de partículas submicrónicas de BaTiO3. Para ello se han realizado ensayos de dilatometría a 10ºC/min hasta 1400ºC. De acuerdo con el comportamiento observado en las curvas de contracción, se realizaron enfriamientos bruscos de muestras a diferentes temperaturas y se estudió la microestructura de las mismas mediante Microscopía Electrónica de Barrido (MEB) sobre superficies de fractura de dichas muestras. Durante el estado inicial de la sinterización de partículas submicrónicas de BaTiO3 se produce un engrosamiento anormal de las mismas, llegando a doblar su tamaño original. Este fenómeno podría contribuir a la densificación del material de acuerdo con un mecanismo de engrosamiento y re-empaquetamiento.