Bubble Wrap-like Carbon-Coated Rattle-Type silica@silicon Nanoparticles as Hybrid Anode Materials for Lithium-Ion Batteries via Surface-Protected Etching

Abstract

Severe volumetric expansion (~400%) limits practical application of silicon nanoparticles as anode materials for next-generation lithium-ion batteries (LIBs). Here, we describe the fabrication and characterization of a conformal polydopamine carbon shell encapsulating rattle-type silica@silicon nanoparticles (PDA–PEI@PVP–SiO2@Si) with a tunable void structure using a dual template strategy with TEOS and (3-aminopropyl)triethoxysilane (APTES) pretreated with polyvinylpyrrolidone (PVP K30) as SiO2 sacrificial template via a modified Stöber process. Polyethylene imine (PEI) crosslinking facilitated the construction of an interconnected three-dimensional bubble wrap-like carbon matrix structure through hydrothermal treatment, pyrolysis, and subsequent surface-protected etching. The composite anode material delivered satisfactory capacities of 539 mAh g−1 after 100 cycles at 0.1 A g−1, 512.76 mAh g−1 after 200 cycles at 1 A g−1, and 453 mAh g−1 rate performance at 5 A g−1, respectively. The electrochemical performance of PDA–PEI@PVP–SiO2@Si was attributed to the rattle-type structure providing void space for Si volume expansion, PVP K30-pretreated APTES/TEOS SiO2 seeds via catalyst-free, hydrothermal-assisted Stöber protecting Si/C spheres upon etching, carbon coating strategy increasing Si conductivity while stabilizing the solid electrolyte interface (SEI), and PEI carbon crosslinks providing continuous conductive pathways across the electrode structure. The present work describes a promising strategy to synthesize tunable yolk shell C@void@Si composite anode materials for high power/energy-density LIBs applications.

Keywords

• lithium-ion battery
• silicon anode
• carbon nanomaterials
• silica coating
• yolk shell structure
• surface protected etching