Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 2000)

Efecto de los aditivos en la formación y estabilidad térmica a baja temperatura del titanato de aluminio

  • Barrios de Arenas, I.,
  • Arenas, F.,
  • Cho, S. A.,
  • Martínez, S.,
  • Sicardi, R.

Journal volume & issue
Vol. 39, no. 6
pp. 699 – 703

Abstract

Read online

This work presents the study of the effect of 3 wt% V2O5, Na2O, CaO and FeTiO3 on the stabilization of Aluminum Titanate (Al2TiO5). Samples were prepared by the conventional processing route of dry ball milling followed by wet mixing and final uniaxial pressing at 300 MPa before sintering at 1400ºC. Specimens were heat treated at 1000ºC during 12 and 20 hours in order to evaluate Al2TiO5 decomposition. The microstructure was observed by Scanning Electron Microscopy (SEM) and phases present were determined by X Ray Diffraction (XRD) and Energy Dispersive Spectroscopy (EDS). It has been elucidated the effect of FeTiO3 (Ilmenite) on the improvement of the formation and thermal stabilization of Al2TiO5.<br><br>En este trabajo se presenta el estudio del efecto de la adición de 3% en peso de V2O5, Na2O, CaO y FeTiO3 en la estabilización térmica del Titanato de Aluminio (Al2TiO5). El procesamiento de las muestras fue mediante la molienda en seco de los polvos de alúmina y titania, mezcla vía húmeda con alcohol isopropílico y sinterización a 1400ºC de los compactos prensados uniaxialmente a 300 MPa. Una vez sinterizadas las muestras fueron tratadas térmicamente a 1000ºC durante 12 y 20 horas para evaluar la descomposición del Al2TiO5. La microestructura de las probetas se analizó mediante Microscopía Electrónica de Barrido (MEB) y las fases presentes se determinaron mediante Difracción de Rayos X (DRX) y Espectroscopía de Rayos X por dispersión de Energía (EDX). Esta caracterización evidenció el efecto beneficioso de la adición de FeTiO3 (Ilmenita) en la formación y estabilización térmica del Al2TiO5.

Keywords