Mechanical Spectroscopy Investigation of Point Defect-Driven Phenomena in a Cr Martensitic Steel

Abstract

The paper presents and discusses results of mechanical spectroscopy (MS) tests carried out on a Cr martensitic steel. The study regards the following topics: (i) embrittlement induced by Cr segregation; (ii) interaction of hydrogen with C⁻Cr associates; (iii) nucleation of Cr carbides. The MS technique permitted characterising of the specific role played by point defects in the investigated phenomena: (i) Cr segregation depends on C⁻Cr associates distribution in as-quenched material, in particular, a slow cooling rate (~150 K/min) from austenitic field involves an unstable distribution, which leads to Cr concentration fluctuations after tempering at 973 K; (ii) hydrogen interacts with C⁻Cr associates, and the phenomenon hinders hydrogen attack (HA) because hydrogen atoms bound by C⁻Cr associates are not able to diffuse towards grain boundaries and dislocation where CH4 bubbles may nucleate, grow, and merge to form the typical HA cracks; (iii) C⁻Cr associates take part in the nucleation mechanism of Cr7C3 carbides, and specifically these carbides form by the aggregation of C⁻Cr associates with 1 Cr atom.

Keywords

• mechanical spectroscopy
• Cr martensitic steel
• point defects