Effect of Relative Thickness Reduction and Heat Treatment on AMS 5596 Sheet Mechanical Properties After Flow Forming

Abstract

In the paper the results of experimental research of the process of flow forming of cylindrical drawpieces were presented. The drawpieces were made of the 3.1 mm thick AMS 5596 sheet by drawing process. Tests were performed on two-roller metal spinning machine of a vertical axis Leifeld SFC 800 V500. The main purpose of this research was to determine the relationship between relative thickness reduction and the mechanical properties of tested material. Knowledge of these dependencies is especially useful in designing machines’ components manufactured by flow forming, in the selection of parameters of realization of this technological process as well. Mechanical properties were determined on the basis of uniaxial tensile of the micro samples obtained from the drawpieces: (I) after cold flow forming, (II) after cold flow forming and in-process heat treatment. Obtained results were shown graphically in the diagrams and their analysis was carried out. In addition, the microstructure of the sheet material tested after drawing and flow forming is presented.

Keywords

• metal spinning
• ams 5596 sheet
• flow forming
• heat treatment
• yield strength