Mixed Metal Oxides of the Type CoxZn1-xFe2O4 as Photocatalysts for Malachite Green Degradation Under UV Light Irradiation

Abstract

A combination of thermal and mechanical (high energy ball milling) treatment was applied in an attempt to obtain polycrystalline mixed metal binary and ternary oxides of the type CoxZn1-xFe2O4 (x=0; 0.25; 0.5; 0.75; 1). The synthetic procedure used successfully produced single-phased, homogeneous ZnFe2O4, CoFe2O4, and Co0.75Zn0.25Fe2O4, as well as mixed oxides, whose composition depended both on the duration of the high energy ball milling and the ratio Zn(II)/Co(II). The formation of spinel-like structures was proved by XRD, Mössbauer spectroscopy and Raman spectroscopy. For the characterization of the samples low-temperature N2 adsorption, UV/Vis spectroscopy and transmission electron microscopy were applied. The energy band gap of the samples was calculated, suggesting they are promising photocatalysts. The decomposition of the Malachite Green in model water solutions under UV-light irradiation was successfully achieved in the presence of the samples as photocatalysts. The highest rate constant was obtained for the sample synthesized at longer milling time in combination with higher Zn(II)/Co(II) ratio. The photocatalytic activity of the ternary mixed oxides was compared with the pure hematite, α-Fe2O3, and the binary ZnFe2O4 and CoFe2O4 ferrites with spinel structure that were treated in the same way. A synergetic effect of α-Fe2O3 and the spinel-like structure on the photocatalytic properties of ternary mixed metal oxide was detected.

Keywords

• ferrites
• mechanoactivation
• Mossbauer spectroscopy
• powder diffraction
• photocatalysis
• malachite green