Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2006)
Procesamiento cerámico de β-TCP para la fabricación de piezas implantables
Abstract
This work describes a method for obtaining large-scale productions of β-TCP by mass-precipitation from calcium and phosphate solutions. The setting of the synthesis conditions was made by studying operational parameters like the concentrations of the reagents, the speed of the mixing of the reagents, pH of precipitation and ageing of the precipitate. This synthesis procedure allows obtaining high purity β-TCP under ASTM F1088-87. Starting from synthesized β-TCP were made rods for implantation by die pressing, slip casting, gel casting and low pressure injection moulding. These rods were well characterized and implanted in Beagle dogs. Thin film histological results for 2, 7, and 14 months of implantation period, shown a good biocompatibility for the material and its resorbable behaviour.<br><br>El trabajo describe la puesta a punto de un método de obtención de grandes cantidades de fosfato tricálcico (β-TCP), por precipitación a partir de disoluciones de sales de calcio y de fosfatos. Para ello se estudia la influencia de los parámetros de operación tales como concentración de reactivos, velocidad de adición, pH de precipitación y tiempo de envejecimiento del precipitado. El procedimiento, que es escalable a nivel industrial, permite obtener β-TCP de elevada pureza, que cumple ASTM F1088-87. Con el material obtenido se procesan barras implantables por prensado, colado, gel-casting e inyección, que se caracterizan detalladamente, y posteriormente se implantan en la tibia de perros Beagle. El estudio histológico en lámina delgada de los implantes, tras períodos de implantación de 2, 7 y 14 meses, permite evaluar la excelente biocompatibilidad del material y su carácter reabsorbible.