Solution Precursor Plasma Spraying of TiO₂ Coatings Using a Catalyst-Free Precursor

Abstract

The microstructural characteristics and phase composition of solution precursor plasma-sprayed (SPPS) titania-based coatings using a catalyst-free precursor are reported in this work. An ethanol-based solution containing titanium isopropoxide was used to deposit TiO2 coatings. The thermal behavior of the solution precursor changed as its phase transformation temperature increased when the molar concentration was increased from 0.3 M to 0.6 M. Scanning electron micrographs showed that the surface of the coatings was composed of nano- and submicron-sized spherical particles (2 in coatings sprayed with various concentrations at various stand-off distances. More detailed discussion is presented with respect to the effects of the solution concentration, stand-off distance, and number of spray passes on the coating’s phase composition and microstructure.

Keywords

• titanium dioxide
• solution precursor plasma spraying
• microstructure