Wettability Behaviour of Metal Surfaces after Sequential Nanosecond and Picosecond Laser Texturing

Abstract

This study examines the wettability behaviour of 304 stainless steel (304SS) and Ti-6Al-4V (Ti64) surfaces after sequential nanosecond (ns) and picosecond (ps) laser texturing; in particular, how the multi-scale surface structures created influence the lifecycle of surface hydrophobicity. The effect of different post-process treatments is also examined. Surfaces were analysed using Scanning Electron Microscopy (SEM), a white light interferometer optical profiler, and Energy Dispersive X-ray (EDX) spectroscopy. Wettability was assessed through sessile drop contact angle (CA) measurements, conducted at regular intervals over periods of up to 12 months, while EDX scans monitored elemental chemical changes. The results show that sequential (ns + ps) laser processing produced multi-scale surface texture with laser-induced periodic surface structures (LIPSS). Compared to the ns laser case, the (ns + ps) laser processed surfaces transitioned more rapidly to a hydrophobic state and maintained this property for much longer, especially when the single post-process treatment was ultrasonic cleaning. Some interesting features in CA development over these extended timescales are revealed. For 304SS, hydrophobicity was reached in 1–2 days, with the CA then remaining in the range of 120 to 140° for up to 180 days; whereas the ns laser-processed surfaces took longer to reach hydrophobicity and only maintained the condition for up to 30 days. Similar results were found for the case of Ti64. The findings show that such multi-scale structured metal surfaces can offer relatively stable hydrophobic properties, the lifetime of which can be extended significantly through the appropriate selection of laser process parameters and post-process treatment. The addition of LIPSS appears to help extend the longevity of the hydrophobic property. In seeking to identify other factors influencing wettability, from our EDX results, we observed a significant and steady rate of increase in the carbon content at the surface over the study period.

Keywords

• laser processing
• surface modification
• laser induced periodic surface structures (LIPSS)
• hydrophobic surface
• post-processing
• wettability