Non-Destructive Testing of Magnetically Impelled Arc Butt Welding of Mild Steel Tubes

Abstract

This paper presents the results of Non-Destructive Testing on Magnetically Impelled Arc Butt (MIAB) welded mild steel tubes of 27mm OD and 1.5mm thickness. As part of this work, the tests covered were radiography, liquid penetrant, and magnetic particle testing. The testing results indicate that porosity, penetration levels and the defects found are within acceptable limits as per standard. For this experimental work, the selection of parameters was based on trial and error adopted in preliminary trials. The irregularities found in the non-destructive testing samples have enabled the fine-tuning of process parameters. The optimum values of hydraulic pressure, weld time and weld current are assessed to be 30-35bar, 5.5s and 150 A, respectively 270 A for this dimension of tubes. This work focuses on the experimental observations of MIAB welding and Non-destructive testing results for MS tubes of the selected dimension, which have not been reported in the existing literature. The achieved input forms the database for the parametric study of this process. The optimum parametric ranges obtained from the results can be extrapolated to be used for joining tubes of different dimensions and can also form the inputs for reaching parameter and response dependency equations.

Keywords

• miab welding
• ndt
• mpt
• lpt
• radiography
• ms1018
• material joining