Environmental Applications of Zeolites: Preparation and Screening of Cu-Modified Zeolites as Potential CO Sensors

Abstract

This work is focused on the application of Cu-containing zeolites as potential environmental sensors for monitoring carbon monoxide. A number of commercial zeolites with different structural properties (NaX, NaY, MOR, FER, BEA and ZSM-5) were modified using CuSO4, Cu(NO3)2 and Cu(OAc)2 solutions as copper sources to prepare Cu+-containing zeolites, since Cu+ forms stable complexes with CO at room temperature that can be monitored by infrared spectroscopy. Zeolite impregnation with Cu(NO3)2 resulted in the highest total Cu-loadings, while the Cu(OAc)2-treated samples had the highest Cu+/Cutotal ratio. Cu(NO3)2-impregnated MOR, which displayed the highest concentration of Cu+, was subjected to a number of tests to evaluate its performance as a potential CO sensor. The working temperature and concentration ranges of the sensor were determined to be from 20 to 300 °C and from 10 to 10,000 ppm, respectively. The stepwise CO desorption experiments indicated that the sensor can be regenerated at 400 °C if required. Additional analyses under realistic flow conditions demonstrated that for hydrophilic zeolites, the co-adsorption of water can compromise the sensor’s performance. Therefore, a hydrophobic Sn-BEA was utilised as a parent material for the preparation of an impregnated Cu-Sn-BEA zeolite, which exhibited superior resistance to interfering water while maintaining its sensing properties. Overall, the prepared Cu-modified zeolites showed promising potential as environmental CO sensors, displaying high sensitivity and selectivity under representative testing conditions.

Keywords

• Cu-modified zeolites
• zeolite-based sensors
• CO monitoring
• IR spectroscopy