Boletín de la Sociedad Española de Cerámica y Vidrio (Oct 1999)
Interacciones hiperfinas en Ba<sub>x</sub>Sr<sub>1-x</sub>HfO<sub>3</sub>
Abstract
In order to determine the microscopic role of cation A in ABO3 perovskites the hyperfine interaction in the Sr1-xBaxHfO3 system using Perturbed Angular Correlation spectroscopy (PAC) is studied. As a previous result the compositions x = 0.50 and 0.25 are shown. The PAC spectra were obtained in the temperature range from 20 to 1000ºC. In both compounds a phase transition to higher symmetry structure was observed at T≈400 and 200ºC, respectively. This structure is proposed to be cubic in both compositions. The results are compared with those obtained in SrHfO3 and BaHfO3.Con el fin de determinar el papel microscópico que juega el catión A en las perovskitas ABO3 se estudia la interacción hiperfina el sistema Sr1-xBaxHfO3 usando la espectroscopia Correlaciones Angulares Perturbadas (PAC) en función de la temperatura y la composición. Como resultado previo se muestra en este trabajo, el estudio de las composiciones x = 0.5 y 0.75. Las medidas PAC se realizaron en el intervalo de temperaturas que va desde 20 a 1000ºC. Para x=0.50 y 0.75 se determinó una transición a una fase de mayor simetría a T≈400 y 200ºC, respectivamente. Se propone que esta fase de mayor simetría es cúbica en ambas composiciones. Los resultados obtenidos son comparados con los compuestos puros SrHfO3 y BaHfO3.