Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 2005)
Estudio por espectroscopía infrarroja de la reacción de obtención de geles de borosilicato con diferentes relaciones Si/B
Abstract
Borosilicate gels with different Si/B ratio have been prepared by the sol-gel method. Such gels were obtained by hydrolysis and further condensation of TEOS (tetraethylorthosilicate) and TEB (triethylborate) alkoxides in acidic aqueous media. The evolution of the Si-O-Si bonds during the sol-gel condensation was dependent on the concentration of boron. Infrared spectroscopy suggested that boron plays an important role on the formation of the siloxane bonds from the hydrolysed TEOS. Thus, the cross-linking of Si-O-Si bonds decreased and the condensation of linear structures increased when the amount of TEB was higher than 10 wt.%. Moreover, it has been observed that this behaviour is directly related with the increase of gelling time in the sols containing significant amount of boron.<br><br>Se ha llevado a cabo el estudio de la formación de diferentes geles de borosilicato preparados mediante la reacción sol-gel de hidrólisis y condensación de los alcóxidos TEOS (tetraetilortosilicato) y TEB (trietilborato) en diferentes proporciones Si/B y en medio acuoso acidulado. La formación de los enlaces Si-O-Si que tiene lugar durante la condensación la reacción sol-gel depende de la cantidad de boro añadido a los diferentes soles. Así, la espectroscopia infrarroja ha puesto de manifiesto que el boro juega un papel determinante en la formación de los enlaces siloxano a partir del TEOS hidrolizado, observándose que el entrecruzamiento de los enlaces Si-O-Si disminuye con el empleo de cantidades de TEB superiores al 10% en peso a la vez que aumenta la condensación en forma de estructuras lineales de los mismos. Además, se pone de manifiesto que este comportamiento está relacionado con el aumento de los tiempos de gelificación observados para altas adiciones de boro.