Preliminary evaluation of production and characterization of wood vinegar from rubberwood

Abstract

This study deals with a slow pyrolysis of rubberwood in a furnace at an atmospheric pressure to produce pyroligneous liquid or wood vinegar. Pyroligneous liquids produced were separated into two fractions based on temperatures in a furnace. The yields of wood vinegar were quantified. Also pH, SG and boiling ranges were determined. The optimum condition of pyrolysis was obtained at the heating rate of 1.4oC/min to the final temperature at 550oC/min with a yield of 27.45%. The pH and specific gravity were attained at about 2.9-3.83 and 1.009-1.027, respectively, depend on process conditions. Also the boiling ranges of rubberwood vinegar approximately were 96-108oC based on the ASTM-D86 method. However, no significantlychanges were seen in the pH, specific gravity and boiling ranges of rubberwood vinegar regarding to hearting rates. For characterization, wood vinegar was fractionated by a distillation into three fractions. Both crude and distilled wood vinegars were analyzed by gas chromatography-mass spectroscopy and gas chromatography. Results showed that the wood vinegar is mainly composed of acetic acid. Also the rubberwood pyrolysis yields high methanol content compared to other woods.

Keywords

• wood vinegar
• pyrolysis
• chemical analysis
• rubberwood