Hardness of Resin Cements Polymerized through Glass-Ceramic Veneers

Abstract

(1) Background: The aim of this study is to evaluate the hardness of resin cements polymerized through ceramic disks under different process factors (ceramic type and thickness, light-polymerization units and polymerization time); (2) Method: Three types of ceramic blocks were used (IPS e.max CAD; Celtra Duo; VITABLOCS). Ceramic disks measuring 0.5 mm, 1.0 mm and 1.5 mm were cut from commercial blocks. Two resin cements (Rely X Veneer and Variolink Esthetic) were polymerized through the ceramic specimens using distinct light-polymerization units (Deep-cure; Blue-phase) and time intervals (10 and 20 s). Hardness of cement specimens was measured using microhardness tester with a Knoop indenter. Data were statistically analyzed using factorial ANOVA (α = 5%); (3) Results: Mean microhardness of Rely X Veneer cement was significantly higher than that of Variolink Esthetic. Deep-cure resulted in higher mean microhardness values compared to Blue-phase at 0.5- and 1-mm specimen thicknesses. Moreover, a direct correlation was found between polymerization time and hardness of resin cement; (4) Conclusions: Surface hardness was affected by resin cement type and ceramic thickness, and not affected by ceramic types, within evaluated conditions. Increasing light-polymerization time significantly increased the hardness of the cement.

Keywords

• resin cement
• veneers
• glass ceramic
• hardness