A Novel Approach for Accelerated Fabrication of Calcium Hydroxyapatite Thin Films

Abstract

In this study we demonstrate, that sol–gel route is suitable to quicker obtain calcium hydroxyapatite (Ca10(PO4)6(OH)2, CHAp) coatings on crystalline Si substrate by modified dip-coating technique. The substrate was dip-coated by precursor and dried for 10 minutes at 200 °C with following cooling using the heating block for 110 min and annealing at 650 °C. Ethylendiamintetraacetic acid and 1,2-ethandiol, and triethanolamine and polyvinyl alcohol were used as complexing agents and as gel network forming agents, respectively. The obtained coatings were characterized by X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), FTIR spectroscopy and contact angle measurements (CAM).

Keywords

• hydroxyapatite
• sol–gel
• dip–coating
• thin film