Applying the Alkali-Activation Method to Encapsulate Silicon Nitride Particles in a Bioactive Matrix for Augmented Strength and Bioactivity
Abstract
The development of bioactive ceramics still poses challenges in finding a good compromise between bioactivity and mechanical robustness. Moreover, a facile, low-cost and energy-saving synthesis technique is still needed. This study concerns the synthesis of a bioactive material by growing a bioactive Na-Ca-Mg-Si-based ceramic matrix produced using the alkali-activation method on silicon nitride (Si3N4) particles. This technique simultaneously forms the matrix precursor and functionalizes the Si3N4 particles’ surface. The optimal strength–bioactivity compromise was found for the composition containing 60 wt.% Si3N4 and 40 wt.% of the matrix exhibiting good compressive strength of up to 110 MPa and extensive precipitation of hydroxyapatite on the sample surface after 7 days of soaking in simulated body fluid. This innovative approach merging strong non-oxide binary ceramics with the versatile and low-cost alkali-activation method holds great expectations for the future in biomaterials.
Keywords